Oxygen transfer phenomenon between slag and molten steel for production of IF steel

《钢铁研究学报:英文版》2020年 第4期 | Yun-qing Ji Chun-yang Liu Hui-xiang Yu Xiao-xuan Deng Fu-xiang Huang Xin-hua Wang   School of Metallurgical and Ecological Engineering University of Science and Technology Beijing Beijing 100083 China Steelmaking Plant Beijing Shougang Co. Ltd. Qian’an 100041 Hebei China Research Institute of Technology Shougang Group Co. Ltd. Beijing 100043 China
导出参考文献 购物车 | ★ 收藏 | 分享
论文服务:
摘 要:FeO-containing slag originated from the basic oxygen furnace to the ladle is a major reoxidation source during the following secondary refining.Ladle slag reduction treatment(slag treatment)is one of the common countermeasures adopted to eliminate the steel contamination by FeO reoxidation.The oxygen transfer phenomenon between molten steel and slag was studied during the industrial production of interstitial-free(IF)steel,the measured and calculated oxygen activities in steel were compared,and the Fe–O equilibrium at the slag–molten steel interface was investigated by thermodynamic analysis.With slag treatment,the oxygen potential is higher in the molten steel than in the pre-deoxidation slag;this causes oxygen transfer from the molten steel to the slag,decreasing the efficiency of slag treatment.Based on this,a two-step slag deoxidation process was optimized.The second step further reduced the FeO content.On the other hand,the CaO/Al2O3(C/A)ratio in the refining slag must be controlled,because it affects the FeO activity and inclusion absorption capacity of the slag.The results suggest that the C/A ratio of 1.2–1.5 and the FeO content of\6%are beneficial to refine IF steel.
【分 类】【工业技术】 > 金属学与金属工艺 > 金属学与热处理
【关键词】 Oxygen transfer IF steel DEOXIDATION Slag treatment Refining slag
【出 处】 《钢铁研究学报:英文版》2020年 第4期 402-408页 共7页
【收 录】 中文科技期刊数据库