Recovery of iron from copper slag via modified roasting in CO-CO2 mixed gas and magnetic separation

《钢铁研究学报:英文版》2020年 第7期 | Ping-guo Jiang Jin-sheng Liu Yi-yu Xiao Xiao-heng Tan Wen-jie Liu   School of Materials Science Shanghai Dianji University Shanghai 201306 China Department of Materials Metallurgy and Chemistry Jiangxi University of Science and Technology Ganzhou 341000 Jiangxi China
导出参考文献 购物车 | ★ 收藏 | 分享
论文服务:
摘 要:A novel technology,modified roasting in CO-CO2 mixed gas and magnetic separation,was presented to recover iron from copper slag.The effects of various parameters such as dosage of flux(CaO),gas flowrate of CO and CO2,roasting temperature,roasting time,particle size of modified slag and magnetic flux density on the oxidized modification and magnetic separation were investigated by comparison of the X-ray diffraction patterns and iron recovery ratio.The optimum conditions for recovering iron by oxidizing roasting and magnetic separation are as follows:calcium oxide content of 25 wt.%,mixed gas flow rates of CO2 and CO of 180 and 20 mL/min,oxidizing roasting at 1323 K for 2 h,grinding the modified slag to 38.5-25.0μm and magnetic separation at 170 mT.The mineralogical and microstructural characteristics of modified slag revealed that the iron-bearing minerals in the copper slag were oxidized,the generated magnetite grew into large particles,and the silicate in copper slag was combined with calcium oxide to form calcium silicate.Finally,the iron-bearing concentrate with an iron grade of 54.79%and iron recovery ratio of 80.14%was effectively obtained.
【分 类】【工业技术】 > 金属学与金属工艺 > 金属学与热处理
【关键词】 Copper slag CO-CO2 mixed gas Modified roasting Magnetic separation Iron recovery ratio
【出 处】 《钢铁研究学报:英文版》2020年 第7期 796-806页 共11页