Fretting wear behaviour of high-nitrogen stainless bearing steel under lubrication condition

《钢铁研究学报:英文版》2020年 第7期 | Huan Lin Mao-sheng Yang Bai-po Shu   College of Materials Science and Engineering Kunming University of Science and Technology Kunming 650093 Yunnan China Institute for Special Steel Central Iron and Steel Research Institute Beijing 100081 China
导出参考文献 购物车 | ★ 收藏 | 分享
论文服务:
摘 要:The fretting wear performance of high-nitrogen stainless bearing steel(40Cr15Mo2VN)under lubrication conditions was researched.Lithium-based grease was preparedusing MoS2 and carbon nanotubes(CNTs)as additives.AISI 52100 steel ball was used in four-ball test to evaluate the extreme pressure property and wear resistance of grease.After four-ball test,the grease adding 0.8 mass%MoS2 and 0.8 mass%CNTs,respectively,was chosen and used for fretting test.AISI 52100 ball and 40Cr15Mo2VN steel disc were used as the upper and lower samples for fretting test.The results showed that wear power consumption increased with the increase in both sliding velocity and contact stress.When initial contact stress was 2.047 GPa,the main wear mechanisms were abrasive wear and plastic deformation as the velocity increased 0.028 to 0.112 m/s.When the velocity was 0.028 m/s,the main wear mechanisms changed abrasive wear to adhesion wear and finally to abrasive wear and adhesion wear as the initial contact stress increased 1.788 to 2.579 GPa.The volume loss grew sharply becaof the changes in wear mechanisms.In this condition,the volume loss growth rate can be divided into three regions according to different wear power consumption ranges corresponding to different wear mechanisms.
【分 类】【工业技术】 > 金属学与金属工艺 > 金属学与热处理
【关键词】 High-nitrogen steel Sliding velocity Contact stress Adhesion wear Abrasive wear Wear power consumption
【出 处】 《钢铁研究学报:英文版》2020年 第7期 849-866页 共18页