摘 要:
对150mm×150mm连铸坯轧制中12mmSCM435合金冷镦钢（％：0．35C、0．98Cr、0．16Mo）盘条的工艺试验表明：采用1020℃加热，900℃轧制，吐丝温度控制在780—800℃，相变前冷却速度控制在1℃／s左右，该钢可以获得均匀的铁素体＋珠光体组织和良好的冷镦性能。[著者文摘]
文章出处:
《特殊钢》-2008年1期 -45-47页
Special Steel
栏目信息:
分 类 号:
相关文章:
Controlled Rolling and Cooling Process for Wire Rod Coil of Cold Heading Alloy Steel SCM435
Duan Guisheng （ 1 School of Metallurgical and Ecological Engineering, University of Science and Technology, Beijing 100083 ; 2 Technical Center, Anyang Iron and Steel Co Ltd, Anyang 455004）
Abstract:
The test results of process for qbl2 mm SCM435 alloy steel （0. 35C, 0. 98Cr, 0. 16Mo） coil rolled by 150 mm × 150 mm concasting billet showed that the uniform structure of ferrite ＋ pearlite and excellent cold heading performance of steel were got by heating billet at 1 020 ℃, rolling at 900 ℃, controlling spinning temperature at 780 - 800 ℃ and cooling rate before phase transformation 1 ℃/s. Material Index Cold Heading Steel SCM435, Wire Rod Coil, Controlled Rolling and Cooling[著者文摘]
Key words:
Cold Heading Steel SCM435, Wire Rod Coil, Controlled Rolling and Cooling